Aluminum Laminated Film for Pouch Cell Case, 100mm W x 210mm L 50pcs/Bag - ALF100210

Product image 1

Aluminum Laminated Film for Pouch Cell Case, 100mm W x 210mm L 50pcs/Bag - ALF100210

This aluminum laminated film (111 um) is used as casing material for polymer Li-Ion battery,50pcs/Bag.

Specifications

Layers from outside to inside

(Material in bracket)

  • Polyamide (JIS Z1714): 0.025mm(+-0.0025mm)
  • Adhesive (Polyester-polyurethane): 4-5g/m2
  • Aluminum foil (JIS A8021): 0.040mm(+-0.004mm)
  • Adhesive (Urethane-free Adhesive): 2-3g/m2
  • Polypropylene: 0.040mm(+-0.004mm)

Thickness:

  • 111μm±11μm

Width

  • 100mm

Length

  • 210mm

Surface quality

  • Matt finish

Pinholes

  • Subject to the applicable aluminum foil standard

Impurity

  • 1mm or less in diameter

Fisheye

  • 2mm or less in diameter(clear),1mm or less in diameter(colored)

Moisture Vapor / O2 Transmission Rate
  • 200ppm / 5 years @ 300K

Laminate strength

  • Nylon/Al more than 2N/15mm
  • Al/CPP more than 5N/15mm

Heat seal strength

  • More than 29.4N/15mm wide at 200x 0.2Mpa x2 sec by MTI's heat sealing equipmentMSK-140 and MSK-115A (Updated from VS-300)

Remained solvent

  • Less than 5mg/m2

Appearance

  • Within the sample of the limit

Slip factor

  • CPP/CPP less than 1.0

 

Click the picture below to see the finished 
polymer Li-Ion battery made by heated sealer

Click the video below to see how to make pouch cell

$48.82

Original: $139.50

-65%
Aluminum Laminated Film for Pouch Cell Case, 100mm W x 210mm L 50pcs/Bag - ALF100210—

$139.50

$48.82

Product Information

Shipping & Returns

Description

This aluminum laminated film (111 um) is used as casing material for polymer Li-Ion battery,50pcs/Bag.

Specifications

Layers from outside to inside

(Material in bracket)

  • Polyamide (JIS Z1714): 0.025mm(+-0.0025mm)
  • Adhesive (Polyester-polyurethane): 4-5g/m2
  • Aluminum foil (JIS A8021): 0.040mm(+-0.004mm)
  • Adhesive (Urethane-free Adhesive): 2-3g/m2
  • Polypropylene: 0.040mm(+-0.004mm)

Thickness:

  • 111μm±11μm

Width

  • 100mm

Length

  • 210mm

Surface quality

  • Matt finish

Pinholes

  • Subject to the applicable aluminum foil standard

Impurity

  • 1mm or less in diameter

Fisheye

  • 2mm or less in diameter(clear),1mm or less in diameter(colored)

Moisture Vapor / O2 Transmission Rate
  • 200ppm / 5 years @ 300K

Laminate strength

  • Nylon/Al more than 2N/15mm
  • Al/CPP more than 5N/15mm

Heat seal strength

  • More than 29.4N/15mm wide at 200x 0.2Mpa x2 sec by MTI's heat sealing equipmentMSK-140 and MSK-115A (Updated from VS-300)

Remained solvent

  • Less than 5mg/m2

Appearance

  • Within the sample of the limit

Slip factor

  • CPP/CPP less than 1.0

 

Click the picture below to see the finished 
polymer Li-Ion battery made by heated sealer

Click the video below to see how to make pouch cell

Aluminum Laminated Film for Pouch Cell Case, 100mm W x 210mm L 50pcs/Bag - ALF100210 | MTI Online Store