Double Side LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM811

Product image 1

Double Side LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM811

The NCM811-coated aluminum foil in a roll can be used as cathode for pouch cell testing. 

SPECIFICATIONS

NCM523 coating
  • Coating Thickness: ~64 um (double side coated) 
  • Total Thickness: ~80 um
    Foil Thickness: ~15-16 um
  • Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll
  • Double sides material density: 21 ± 0.4 mg/cm2
  • Compaction density: 3.3 ± 0.1 g/cm3
  • Active Material Proportion in Powder: 95% (PVDF and Super P is 2% and 3%, respectively) 
Specific Capacity

 

190 mAh/g


$521.50

Original: $1,490.00

-65%
Double Side LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM811—

$1,490.00

$521.50

Product Information

Shipping & Returns

Description

The NCM811-coated aluminum foil in a roll can be used as cathode for pouch cell testing. 

SPECIFICATIONS

NCM523 coating
  • Coating Thickness: ~64 um (double side coated) 
  • Total Thickness: ~80 um
    Foil Thickness: ~15-16 um
  • Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll
  • Double sides material density: 21 ± 0.4 mg/cm2
  • Compaction density: 3.3 ± 0.1 g/cm3
  • Active Material Proportion in Powder: 95% (PVDF and Super P is 2% and 3%, respectively) 
Specific Capacity

 

190 mAh/g


Double Side LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM811 | MTI Online Store