Polyvinylidene Fluoride (PVDF-HFP) as Binder for Battery Electrode, 100g/bottle -Lib-PVDF-HFP

Product image 1

Polyvinylidene Fluoride (PVDF-HFP) as Binder for Battery Electrode, 100g/bottle -Lib-PVDF-HFP

Solef-215010 PVDF is suitable for extrusion and solution processing in lithium battery application. It can be used for PVDF electrolyte membranes, or it can be used as slurry coating for the separator.

SPECIFICATION:

Quantity
  • 100 g/bottle
Specific Gravity 
  • 1.75-1.80

Melt Flow Rate

(MFR @ 23 °C, 5.0 kg)
  • 3.0 - 9.0 g/10min
Water Absorption (24h, 23 °C)
  • <0.040 %
Young's Modulus (23 °C, 2.00 mm)
  • 360-480 MPa
Tensile Strength (Yield, 23 °C, 2.00 mm
  • 15.0-18.0 MPa
Tensile Strength (Break, 23 °C, 2.00 mm)
  • 20.0-40.0 MPa
Tensile Elongation (Yield, 23 °C, 2.00 mm)
  • 12%-15%
Tensile Elongation (Break, 23 °C, 2.00 mm)
  • 600%-750%
Glassy Transition Temperature (Tg)
  • -40.0 °C
Melting Point
  • 130-136 °C
Peak Crystallization Temperature (DSC)
  • 89.0-93.0 °C 
Heating of Fusion
  • 20.0-24.0 J/g
Surface Resistivity
  • > 1.0E+14 Ω
Volume Resistivity
  • > 1.0E+14 Ωcm

 

 

 

$69.65

Original: $199.00

-65%
Polyvinylidene Fluoride (PVDF-HFP) as Binder for Battery Electrode, 100g/bottle -Lib-PVDF-HFP—

$199.00

$69.65

Product Information

Shipping & Returns

Description

Solef-215010 PVDF is suitable for extrusion and solution processing in lithium battery application. It can be used for PVDF electrolyte membranes, or it can be used as slurry coating for the separator.

SPECIFICATION:

Quantity
  • 100 g/bottle
Specific Gravity 
  • 1.75-1.80

Melt Flow Rate

(MFR @ 23 °C, 5.0 kg)
  • 3.0 - 9.0 g/10min
Water Absorption (24h, 23 °C)
  • <0.040 %
Young's Modulus (23 °C, 2.00 mm)
  • 360-480 MPa
Tensile Strength (Yield, 23 °C, 2.00 mm
  • 15.0-18.0 MPa
Tensile Strength (Break, 23 °C, 2.00 mm)
  • 20.0-40.0 MPa
Tensile Elongation (Yield, 23 °C, 2.00 mm)
  • 12%-15%
Tensile Elongation (Break, 23 °C, 2.00 mm)
  • 600%-750%
Glassy Transition Temperature (Tg)
  • -40.0 °C
Melting Point
  • 130-136 °C
Peak Crystallization Temperature (DSC)
  • 89.0-93.0 °C 
Heating of Fusion
  • 20.0-24.0 J/g
Surface Resistivity
  • > 1.0E+14 Ω
Volume Resistivity
  • > 1.0E+14 Ωcm

 

 

 

Polyvinylidene Fluoride (PVDF-HFP) as Binder for Battery Electrode, 100g/bottle -Lib-PVDF-HFP | MTI Online Store