Lithium Polyacrylate (LiPAA. or LA136DL) Aqueous Binder for Silicon-Based Anode, 200 g/bottle - Lib-LiPAA

Product image 1

Lithium Polyacrylate (LiPAA. or LA136DL) Aqueous Binder for Silicon-Based Anode, 200 g/bottle - Lib-LiPAA

Lithium polyacrylate (LiPAA or called LA-136DL) binder is a water-soluble polyacrylate with abundant functional groups. The carboxyl groups can form strong hydrogen bonds with both active material and current collector. It is widely used for slurry preparation of silicon-based anode material, LiFePO4, lithium sulfur battery, and sodium ion battery electrode. Compared with the Carboxymethyl cellulose (CMC) binder, the silicon anode using LiPAA binder has better cycling performance.

Specifications:
  • Appearance: Milky white liquid with a light yellow.
  • Average molecular weight of LiPAA: ~700000
  • Solidity: 6% +/- 0.3% (wt%)
  • PH: 7-8
  • Viscosity (40°C): 9000-13000 mPa. S
  • No antioxidants added
  • SDS: Safety Data Sheet

 

Application Notes:

  • Please click to see Step by Step Recipe for Preparing Anode & Cathode Electrode Slurry
  • Tips: You may use a binder like below:
    • Cathode: Cathode Powder+Conductive Graphite+PVDF+NMP 
    • Anode: Silicon Anode Powder+Condcutive Graphite+PAA
  • You may use Digital Battery Electrode Paste/Slurry Viscosity Tester to achieve consistent slurry
  • Please well mix the solution and make sure the binder is disolved into solution ( Vacuum mixer is better )
  • The product is not warranted if you use for other applications rather Li-Ion anode slurry
$31.15

Original: $89.00

-65%
Lithium Polyacrylate (LiPAA. or LA136DL) Aqueous Binder for Silicon-Based Anode, 200 g/bottle - Lib-LiPAA—

$89.00

$31.15

Product Information

Shipping & Returns

Description

Lithium polyacrylate (LiPAA or called LA-136DL) binder is a water-soluble polyacrylate with abundant functional groups. The carboxyl groups can form strong hydrogen bonds with both active material and current collector. It is widely used for slurry preparation of silicon-based anode material, LiFePO4, lithium sulfur battery, and sodium ion battery electrode. Compared with the Carboxymethyl cellulose (CMC) binder, the silicon anode using LiPAA binder has better cycling performance.

Specifications:
  • Appearance: Milky white liquid with a light yellow.
  • Average molecular weight of LiPAA: ~700000
  • Solidity: 6% +/- 0.3% (wt%)
  • PH: 7-8
  • Viscosity (40°C): 9000-13000 mPa. S
  • No antioxidants added
  • SDS: Safety Data Sheet

 

Application Notes:

  • Please click to see Step by Step Recipe for Preparing Anode & Cathode Electrode Slurry
  • Tips: You may use a binder like below:
    • Cathode: Cathode Powder+Conductive Graphite+PVDF+NMP 
    • Anode: Silicon Anode Powder+Condcutive Graphite+PAA
  • You may use Digital Battery Electrode Paste/Slurry Viscosity Tester to achieve consistent slurry
  • Please well mix the solution and make sure the binder is disolved into solution ( Vacuum mixer is better )
  • The product is not warranted if you use for other applications rather Li-Ion anode slurry
Lithium Polyacrylate (LiPAA. or LA136DL) Aqueous Binder for Silicon-Based Anode, 200 g/bottle - Lib-LiPAA | MTI Online Store